EN AW-6012 initial T3 tensile and hardness reference (CC BY experimental)
EN AW-6012 AlMgSiPb, initial T3 | source form not stated; machined round tensile specimen
|
|---|---|
| Density |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
75.0 GPa
Young's modulus
Experimental Measured Screening
EN AW-6012 AlMgSiPb, initial T3; room-temperature uniaxial tensile test on 8 mm diameter round specimens at initial strain rate 2.5e-4 1/s; tensile values are six-measurement means
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
309.0 MPa
Tensile yield strength
Experimental Measured Screening
EN AW-6012 AlMgSiPb, initial T3; room-temperature uniaxial tensile test on 8 mm diameter round specimens at initial strain rate 2.5e-4 1/s; tensile values are six-measurement means
|
| Tensile strength |
350.0 MPa
Ultimate tensile strength
Experimental Measured Screening
EN AW-6012 AlMgSiPb, initial T3; room-temperature uniaxial tensile test on 8 mm diameter round specimens at initial strain rate 2.5e-4 1/s; tensile values are six-measurement means
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|