| Property |
EN AW-5049-O seamless tube tensile population (CC BY experimental)
fully annealed EN AW-5049-O thin-wall seamless tube | thin-wall seamless round tube
|
|---|---|
| Density |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
71.69 MPa
Tensile yield strength
Experimental Measured Screening
fully annealed EN AW-5049-O seamless tube, 32.00 mm outside diameter, 1.50 mm nominal wall, same tube batch; longitudinal ASTM E8 tensile specimens cut at 0, 90, 180 and 270 deg positions; Instron test at room temperature and reported machine velocity 1.4 mm/min
73.36 MPa
Tensile yield strength at 0 deg circumferential position
Experimental Measured Screening
fully annealed EN AW-5049-O seamless tube, 32.00 mm outside diameter, 1.50 mm nominal wall, same tube batch; longitudinal ASTM E8 tensile specimens cut at 0, 90, 180 and 270 deg positions; Instron test at room temperature and reported machine velocity 1.4 mm/min; specimen cut at 0 deg circumferential position
73.69 MPa
Tensile yield strength at 90 deg circumferential position
Experimental Measured Screening
fully annealed EN AW-5049-O seamless tube, 32.00 mm outside diameter, 1.50 mm nominal wall, same tube batch; longitudinal ASTM E8 tensile specimens cut at 0, 90, 180 and 270 deg positions; Instron test at room temperature and reported machine velocity 1.4 mm/min; specimen cut at 90 deg circumferential position
69.22 MPa
Tensile yield strength at 180 deg circumferential position
Experimental Measured Screening
fully annealed EN AW-5049-O seamless tube, 32.00 mm outside diameter, 1.50 mm nominal wall, same tube batch; longitudinal ASTM E8 tensile specimens cut at 0, 90, 180 and 270 deg positions; Instron test at room temperature and reported machine velocity 1.4 mm/min; specimen cut at 180 deg circumferential position
70.5 MPa
Tensile yield strength at 270 deg circumferential position
Experimental Measured Screening
fully annealed EN AW-5049-O seamless tube, 32.00 mm outside diameter, 1.50 mm nominal wall, same tube batch; longitudinal ASTM E8 tensile specimens cut at 0, 90, 180 and 270 deg positions; Instron test at room temperature and reported machine velocity 1.4 mm/min; specimen cut at 270 deg circumferential position
|
| Tensile strength |
225.5 MPa
Ultimate tensile strength
Experimental Measured Screening
fully annealed EN AW-5049-O seamless tube, 32.00 mm outside diameter, 1.50 mm nominal wall, same tube batch; longitudinal ASTM E8 tensile specimens cut at 0, 90, 180 and 270 deg positions; Instron test at room temperature and reported machine velocity 1.4 mm/min
226.47 MPa
Ultimate tensile strength at 0 deg circumferential position
Experimental Measured Screening
fully annealed EN AW-5049-O seamless tube, 32.00 mm outside diameter, 1.50 mm nominal wall, same tube batch; longitudinal ASTM E8 tensile specimens cut at 0, 90, 180 and 270 deg positions; Instron test at room temperature and reported machine velocity 1.4 mm/min; specimen cut at 0 deg circumferential position
227.7 MPa
Ultimate tensile strength at 90 deg circumferential position
Experimental Measured Screening
fully annealed EN AW-5049-O seamless tube, 32.00 mm outside diameter, 1.50 mm nominal wall, same tube batch; longitudinal ASTM E8 tensile specimens cut at 0, 90, 180 and 270 deg positions; Instron test at room temperature and reported machine velocity 1.4 mm/min; specimen cut at 90 deg circumferential position
224.61 MPa
Ultimate tensile strength at 180 deg circumferential position
Experimental Measured Screening
fully annealed EN AW-5049-O seamless tube, 32.00 mm outside diameter, 1.50 mm nominal wall, same tube batch; longitudinal ASTM E8 tensile specimens cut at 0, 90, 180 and 270 deg positions; Instron test at room temperature and reported machine velocity 1.4 mm/min; specimen cut at 180 deg circumferential position
223.2 MPa
Ultimate tensile strength at 270 deg circumferential position
Experimental Measured Screening
fully annealed EN AW-5049-O seamless tube, 32.00 mm outside diameter, 1.50 mm nominal wall, same tube batch; longitudinal ASTM E8 tensile specimens cut at 0, 90, 180 and 270 deg positions; Instron test at room temperature and reported machine velocity 1.4 mm/min; specimen cut at 270 deg circumferential position
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|