| Property |
AA3004 cast condition A6, compression reference (CC BY experimental)
laboratory permanent-mold cast AA3004, condition A6 | laboratory permanent-mold cast ingot; machined compression specimen
|
|---|---|
| Density |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
86.2 MPa
Compression yield strength at room temperature
Experimental Measured Screening
laboratory AA3004 permanent-mold casting (Al-1.2Mn-1.1Mg-0.6Fe-0.25Si wt.%), 10 mm diameter x 15 mm compression specimen; three-test mean; strain rate 10^-3 1/s; condition A6, 625 degC for 4 h, followed by direct water quench to room temperature
59.3 MPa
Compression yield strength at 300 degC
Experimental Measured Screening
laboratory AA3004 permanent-mold casting (Al-1.2Mn-1.1Mg-0.6Fe-0.25Si wt.%), 10 mm diameter x 15 mm compression specimen; three-test mean; strain rate 10^-3 1/s; condition A6, 625 degC for 4 h, followed by direct water quench to room temperature
|
| Tensile strength |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|