AA5182 finally annealed sheet, 1 mm, 90 degree direction (CC BY experimental)
AA5182 sheet produced by industrial twin-roll continuous casting and thermomechanical rolling, finally annealed at 400 degC for 4 h | sheet
|
|---|---|
| Density |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
112.0 MPa
Tensile yield strength, 90 deg
Experimental Measured Screening
AA5182 twin-roll-cast and thermomechanically processed 1 mm sheet after final annealing at 400 degC for 4 h; tensile direction 90 deg to casting direction; reported average with 95% confidence interval
|
| Tensile strength |
260.0 MPa
Ultimate tensile strength, 90 deg
Experimental Measured Screening
AA5182 twin-roll-cast and thermomechanically processed 1 mm sheet after final annealing at 400 degC for 4 h; tensile direction 90 deg to casting direction; reported average with 95% confidence interval
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|