Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
AA6005-T6 extruded plate, 2 mm, ED (CC BY experimental)
AA6005-T6 industrially cast, hot-extruded, water-quenched and artificially aged plate | hot-extruded plate
|
|---|---|
| Density |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
270.0 MPa
Tensile yield strength, ED
Experimental Measured Screening
AA6005-T6 plate, 2 mm thick x 110 mm wide, industrial DC-cast billet, homogenized 560 degC for 12 h, hot extruded at 530 degC, water quenched and aged 170 degC for 12 h; ambient tensile test at 6.7e-4 1/s; three repeats; extrusion direction (ED)
|
| Tensile strength |
295.0 MPa
Ultimate tensile strength, ED
Experimental Measured Screening
AA6005-T6 plate, 2 mm thick x 110 mm wide, industrial DC-cast billet, homogenized 560 degC for 12 h, hot extruded at 530 degC, water quenched and aged 170 degC for 12 h; ambient tensile test at 6.7e-4 1/s; three repeats; extrusion direction (ED)
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|