AA7005 hot-rolled plate, 3.3 mm, aged 120 degC for 192 h, RD (CC BY experimental)
commercial AA7005 hot-rolled plate, solution treated, water quenched and experimentally peak aged at 120 degC for 192 h | hot-rolled plate
|
|---|---|
| Density |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
340.0 MPa
Tensile yield strength, RD
Experimental Measured Screening
commercial AA7005 hot-rolled plate, 3.3 mm thick; solution treated at 470 degC for 90 min, water quenched, and aged at 120 degC for 192 h; longitudinal tensile loading parallel to rolling direction; room temperature 25 degC; strain rate 1e-3 1/s; five specimens
|
| Tensile strength |
382.0 MPa
Ultimate tensile strength, RD
Experimental Measured Screening
commercial AA7005 hot-rolled plate, 3.3 mm thick; solution treated at 470 degC for 90 min, water quenched, and aged at 120 degC for 192 h; longitudinal tensile loading parallel to rolling direction; room temperature 25 degC; strain rate 1e-3 1/s; five specimens
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|