EN AW-6060-T6 extruded I-beam tensile group 1 (CC BY experimental)
EN AW-6060 peak temper T6; group 1 long flat coupons cut from extruded I-beam I 160 x 88 x 6.5 x 5 | extruded I-beam I 160 x 88 x 6.5 x 5
|
|---|---|
| Density |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
66.4 GPa
Young's modulus
Experimental Measured Screening
EN AW-6060-T6 coupons, 5 mm thick, waterjet cut parallel to extrusion direction from I 160 x 88 x 6.5 x 5 extruded I-beam; six specimens; room-temperature test; group 1, long flat, 50 mm extensometer gauge; 2.0 MPa/s through elastic range, then reported 0.03 mm/s
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
181.5 MPa
Tensile yield strength
Experimental Measured Screening
EN AW-6060-T6 coupons, 5 mm thick, waterjet cut parallel to extrusion direction from I 160 x 88 x 6.5 x 5 extruded I-beam; six specimens; room-temperature test; group 1, long flat, 50 mm extensometer gauge; 2.0 MPa/s through elastic range, then reported 0.03 mm/s
|
| Tensile strength |
209.8 MPa
Ultimate tensile strength
Experimental Measured Screening
EN AW-6060-T6 coupons, 5 mm thick, waterjet cut parallel to extrusion direction from I 160 x 88 x 6.5 x 5 extruded I-beam; six specimens; room-temperature test; group 1, long flat, 50 mm extensometer gauge; 2.0 MPa/s through elastic range, then reported 0.03 mm/s
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|