| Property |
15-5PH H1100 bar/forging (MIL-HDBK-5H)
15-5PH H1100; bar or forging; thickness/diameter <=304.8 mm | bar or forging
|
|---|---|
| Density |
7833 kg/m^3
Density
Historical Nominal
15-5PH H1100; bar or forging; thickness/diameter <=304.8 mm; S-basis
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
196.501 GPa
Young's modulus
Historical Nominal
15-5PH H1100; bar or forging; thickness/diameter <=304.8 mm; S-basis
|
| Shear modulus |
77.221 GPa
Shear modulus
Historical Nominal
15-5PH H1100; bar or forging; thickness/diameter <=304.8 mm; S-basis
|
| Poisson's ratio |
0.27 -
Poisson's ratio
Historical Nominal
15-5PH H1100; bar or forging; thickness/diameter <=304.8 mm; S-basis
|
| Yield strength |
792.897 MPa
Tensile yield strength, L
Historical Public Release Table Value
15-5PH H1100; bar or forging; thickness/diameter <=304.8 mm; S-basis; L direction
792.897 MPa
Tensile yield strength, LT
Historical Public Release Table Value
15-5PH H1100; bar or forging; thickness/diameter <=304.8 mm; S-basis; LT direction
|
| Tensile strength |
965.266 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
15-5PH H1100; bar or forging; thickness/diameter <=304.8 mm; S-basis; L direction
965.266 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
15-5PH H1100; bar or forging; thickness/diameter <=304.8 mm; S-basis; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|