| Property |
17-4PH H900 bar (MIL-HDBK-5H)
17-4PH H900; bar; thickness/diameter <203.2 mm | bar
|
|---|---|
| Density |
7806 kg/m^3
Density
Historical Nominal
17-4PH H900; bar; thickness/diameter <203.2 mm; A-basis
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
196.501 GPa
Young's modulus
Historical Nominal
17-4PH H900; bar; thickness/diameter <203.2 mm; A-basis
|
| Shear modulus |
77.221 GPa
Shear modulus
Historical Nominal
17-4PH H900; bar; thickness/diameter <203.2 mm; A-basis
|
| Poisson's ratio |
0.27 -
Poisson's ratio
Historical Nominal
17-4PH H900; bar; thickness/diameter <203.2 mm; A-basis
|
| Yield strength |
1172.109 MPa
Tensile yield strength, L
Historical Public Release Table Value
17-4PH H900; bar; thickness/diameter <203.2 mm; A-basis; L direction
1172.109 MPa
Compressive yield strength, L
Historical Public Release Table Value
17-4PH H900; bar; thickness/diameter <203.2 mm; A-basis; L direction
|
| Tensile strength |
1310.004 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
17-4PH H900; bar; thickness/diameter <203.2 mm; A-basis; L direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|