| Property |
Aluminum 2024-T3 extrusion, <=6.3 mm (MIL-HDBK-5H)
2024-T3; extruded bar, rod or shape; <=6.3 mm thickness at quench | extruded bar, rod or shape
|
|---|---|
| Density |
2768 kg/m^3
Density
Historical Nominal
2024-T3; extruded bar, rod or shape; <=6.3 mm thickness at quench; A-basis, <=0.249 in T3/T3510/T3511 table column
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
74.463 GPa
Young's modulus
Historical Nominal
2024-T3; extruded bar, rod or shape; <=6.3 mm thickness at quench; A-basis, <=0.249 in T3/T3510/T3511 table column
|
| Shear modulus |
28.269 GPa
Shear modulus
Historical Nominal
2024-T3; extruded bar, rod or shape; <=6.3 mm thickness at quench; A-basis, <=0.249 in T3/T3510/T3511 table column
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
2024-T3; extruded bar, rod or shape; <=6.3 mm thickness at quench; A-basis, <=0.249 in T3/T3510/T3511 table column
|
| Yield strength |
289.58 MPa
Tensile yield strength, L
Historical Public Release Table Value
2024-T3; extruded bar, rod or shape; <=6.3 mm thickness at quench; A-basis, <=0.249 in T3/T3510/T3511 table column; L direction
255.106 MPa
Tensile yield strength, LT
Historical Public Release Table Value
2024-T3; extruded bar, rod or shape; <=6.3 mm thickness at quench; A-basis, <=0.249 in T3/T3510/T3511 table column; LT direction
234.422 MPa
Compressive yield strength, L
Historical Public Release Table Value
2024-T3; extruded bar, rod or shape; <=6.3 mm thickness at quench; A-basis, <=0.249 in T3/T3510/T3511 table column; L direction
282.685 MPa
Compressive yield strength, LT
Historical Public Release Table Value
2024-T3; extruded bar, rod or shape; <=6.3 mm thickness at quench; A-basis, <=0.249 in T3/T3510/T3511 table column; LT direction
|
| Tensile strength |
393.001 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
2024-T3; extruded bar, rod or shape; <=6.3 mm thickness at quench; A-basis, <=0.249 in T3/T3510/T3511 table column; L direction
372.317 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
2024-T3; extruded bar, rod or shape; <=6.3 mm thickness at quench; A-basis, <=0.249 in T3/T3510/T3511 table column; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|