Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Aluminum 2024-T3510/T3511 extrusion, 6.35-19 mm (MIL-HDBK-5H)
2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench | extruded bar, rod or shape
|
|---|---|
| Density |
2768 kg/m^3
Density
Historical Nominal
2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench; lower A-basis value across 0.250-0.499 and 0.500-0.749 in columns
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
74.463 GPa
Young's modulus
Historical Nominal
2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench; lower A-basis value across 0.250-0.499 and 0.500-0.749 in columns
|
| Shear modulus |
28.269 GPa
Shear modulus
Historical Nominal
2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench; lower A-basis value across 0.250-0.499 and 0.500-0.749 in columns
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench; lower A-basis value across 0.250-0.499 and 0.500-0.749 in columns
|
| Yield strength |
303.369 MPa
Tensile yield strength, L
Historical Public Release Table Value
2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench; lower A-basis value across 0.250-0.499 and 0.500-0.749 in columns; L direction
255.106 MPa
Tensile yield strength, LT
Historical Public Release Table Value
2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench; lower A-basis value across 0.250-0.499 and 0.500-0.749 in columns; LT direction
255.106 MPa
Compressive yield strength, L
Historical Public Release Table Value
2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench; lower A-basis value across 0.250-0.499 and 0.500-0.749 in columns; L direction
275.79 MPa
Compressive yield strength, LT
Historical Public Release Table Value
2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench; lower A-basis value across 0.250-0.499 and 0.500-0.749 in columns; LT direction
|
| Tensile strength |
413.685 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench; lower A-basis value across 0.250-0.499 and 0.500-0.749 in columns; L direction
372.317 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench; lower A-basis value across 0.250-0.499 and 0.500-0.749 in columns; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|