Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Aluminum 2024-T4 bar/rod, 3.175-138 mm (MIL-HDBK-5H)
2024-T4; rolled, drawn or cold-finished bar/rod; 3.175-138 mm | rolled, drawn or cold-finished bar or rod
|
|---|---|
| Density |
2768 kg/m^3
Density
Historical Nominal
2024-T4; rolled, drawn or cold-finished bar/rod; 3.175-138 mm; Historical T4 temper; the handbook explicitly says it is obsolete and should not be specified for new designs.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
72.395 GPa
Young's modulus
Historical Nominal
2024-T4; rolled, drawn or cold-finished bar/rod; 3.175-138 mm; Historical T4 temper; the handbook explicitly says it is obsolete and should not be specified for new designs.
|
| Shear modulus |
27.579 GPa
Shear modulus
Historical Nominal
2024-T4; rolled, drawn or cold-finished bar/rod; 3.175-138 mm; Historical T4 temper; the handbook explicitly says it is obsolete and should not be specified for new designs.
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
2024-T4; rolled, drawn or cold-finished bar/rod; 3.175-138 mm; Historical T4 temper; the handbook explicitly says it is obsolete and should not be specified for new designs.
|
| Yield strength |
275.79 MPa
Tensile yield strength, L
Historical Public Release Table Value
2024-T4; rolled, drawn or cold-finished bar/rod; 3.175-138 mm; Historical T4 temper; the handbook explicitly says it is obsolete and should not be specified for new designs.; L direction
248.211 MPa
Tensile yield strength, LT
Historical Public Release Table Value
2024-T4; rolled, drawn or cold-finished bar/rod; 3.175-138 mm; Historical T4 temper; the handbook explicitly says it is obsolete and should not be specified for new designs.; LT direction
220.632 MPa
Compressive yield strength, L
Historical Public Release Table Value
2024-T4; rolled, drawn or cold-finished bar/rod; 3.175-138 mm; Historical T4 temper; the handbook explicitly says it is obsolete and should not be specified for new designs.; L direction
|
| Tensile strength |
427.475 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
2024-T4; rolled, drawn or cold-finished bar/rod; 3.175-138 mm; Historical T4 temper; the handbook explicitly says it is obsolete and should not be specified for new designs.; L direction
358.527 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
2024-T4; rolled, drawn or cold-finished bar/rod; 3.175-138 mm; Historical T4 temper; the handbook explicitly says it is obsolete and should not be specified for new designs.; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|