Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Aluminum 2219-T851 plate, 6.35-63 mm (MIL-HDBK-5H)
2219-T851; plate; 6.35-63 mm | plate
|
|---|---|
| Density |
2851 kg/m^3
Density
Historical Nominal
2219-T851; plate; 6.35-63 mm; lower A-basis value across 0.250-2.480 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
72.395 GPa
Young's modulus
Historical Nominal
2219-T851; plate; 6.35-63 mm; lower A-basis value across 0.250-2.480 in
|
| Shear modulus |
27.579 GPa
Shear modulus
Historical Nominal
2219-T851; plate; 6.35-63 mm; lower A-basis value across 0.250-2.480 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
2219-T851; plate; 6.35-63 mm; lower A-basis value across 0.250-2.480 in
|
| Yield strength |
324.054 MPa
Tensile yield strength, L
Historical Public Release Table Value
2219-T851; plate; 6.35-63 mm; lower A-basis value across 0.250-2.480 in; L direction
310.264 MPa
Tensile yield strength, LT
Historical Public Release Table Value
2219-T851; plate; 6.35-63 mm; lower A-basis value across 0.250-2.480 in; LT direction
324.054 MPa
Compressive yield strength, L
Historical Public Release Table Value
2219-T851; plate; 6.35-63 mm; lower A-basis value across 0.250-2.480 in; L direction
330.948 MPa
Compressive yield strength, LT
Historical Public Release Table Value
2219-T851; plate; 6.35-63 mm; lower A-basis value across 0.250-2.480 in; LT direction
|
| Tensile strength |
420.58 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
2219-T851; plate; 6.35-63 mm; lower A-basis value across 0.250-2.480 in; L direction
427.475 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
2219-T851; plate; 6.35-63 mm; lower A-basis value across 0.250-2.480 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|