Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Aluminum 6061-T6510/T6511 extrusion, <=12.7 mm (MIL-HDBK-5H)
6061-T6510/T6511; extrusion; <=12.7 mm thickness at quench | extruded rod, bar, or shape
|
|---|---|
| Density |
2713 kg/m^3
Density
Historical Nominal
6061-T6510/T6511; extrusion; <=12.7 mm thickness at quench; A-basis, <=1.000 in table column, limited here to <=12.7 mm
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
68.258 GPa
Young's modulus
Historical Nominal
6061-T6510/T6511; extrusion; <=12.7 mm thickness at quench; A-basis, <=1.000 in table column, limited here to <=12.7 mm
|
| Shear modulus |
26.2 GPa
Shear modulus
Historical Nominal
6061-T6510/T6511; extrusion; <=12.7 mm thickness at quench; A-basis, <=1.000 in table column, limited here to <=12.7 mm
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
6061-T6510/T6511; extrusion; <=12.7 mm thickness at quench; A-basis, <=1.000 in table column, limited here to <=12.7 mm
|
| Yield strength |
241.317 MPa
Tensile yield strength, L
Historical Public Release Table Value
6061-T6510/T6511; extrusion; <=12.7 mm thickness at quench; A-basis, <=1.000 in table column, limited here to <=12.7 mm; L direction
227.527 MPa
Tensile yield strength, LT
Historical Public Release Table Value
6061-T6510/T6511; extrusion; <=12.7 mm thickness at quench; A-basis, <=1.000 in table column, limited here to <=12.7 mm; LT direction
234.422 MPa
Compressive yield strength, L
Historical Public Release Table Value
6061-T6510/T6511; extrusion; <=12.7 mm thickness at quench; A-basis, <=1.000 in table column, limited here to <=12.7 mm; L direction
241.317 MPa
Compressive yield strength, LT
Historical Public Release Table Value
6061-T6510/T6511; extrusion; <=12.7 mm thickness at quench; A-basis, <=1.000 in table column, limited here to <=12.7 mm; LT direction
|
| Tensile strength |
262.001 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
6061-T6510/T6511; extrusion; <=12.7 mm thickness at quench; A-basis, <=1.000 in table column, limited here to <=12.7 mm; L direction
255.106 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
6061-T6510/T6511; extrusion; <=12.7 mm thickness at quench; A-basis, <=1.000 in table column, limited here to <=12.7 mm; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|