| Property |
Aluminum 7010-T7651 plate, 12.7-38 mm (MIL-HDBK-5H)
7010-T7651; plate; 12.7-38 mm | plate
|
|---|---|
| Density |
2823 kg/m^3
Density
Historical Nominal
7010-T7651; plate; 12.7-38 mm; S-basis across 0.500-1.500 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
70.327 GPa
Young's modulus
Historical Nominal
7010-T7651; plate; 12.7-38 mm; S-basis across 0.500-1.500 in
|
| Shear modulus |
26.89 GPa
Shear modulus
Historical Nominal
7010-T7651; plate; 12.7-38 mm; S-basis across 0.500-1.500 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7010-T7651; plate; 12.7-38 mm; S-basis across 0.500-1.500 in
|
| Yield strength |
455.054 MPa
Tensile yield strength, L
Historical Public Release Table Value
7010-T7651; plate; 12.7-38 mm; S-basis across 0.500-1.500 in; L direction
455.054 MPa
Tensile yield strength, LT
Historical Public Release Table Value
7010-T7651; plate; 12.7-38 mm; S-basis across 0.500-1.500 in; LT direction
448.159 MPa
Compressive yield strength, L
Historical Public Release Table Value
7010-T7651; plate; 12.7-38 mm; S-basis across 0.500-1.500 in; L direction
461.949 MPa
Compressive yield strength, LT
Historical Public Release Table Value
7010-T7651; plate; 12.7-38 mm; S-basis across 0.500-1.500 in; LT direction
|
| Tensile strength |
524.002 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7010-T7651; plate; 12.7-38 mm; S-basis across 0.500-1.500 in; L direction
524.002 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
7010-T7651; plate; 12.7-38 mm; S-basis across 0.500-1.500 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|