| Property |
Aluminum 7050-T7451 plate, 12.7-100 mm (MIL-HDBK-5H)
7050-T7451; plate; 12.7-100 mm | plate
|
|---|---|
| Density |
2823 kg/m^3
Density
Historical Nominal
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
71.016 GPa
Young's modulus
Historical Nominal
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in
|
| Shear modulus |
26.89 GPa
Shear modulus
Historical Nominal
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in
|
| Yield strength |
427.475 MPa
Tensile yield strength, L
Historical Public Release Table Value
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in; L direction
427.475 MPa
Tensile yield strength, LT
Historical Public Release Table Value
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in; LT direction
413.685 MPa
Compressive yield strength, L
Historical Public Release Table Value
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in; L direction
448.159 MPa
Compressive yield strength, LT
Historical Public Release Table Value
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in; LT direction
393.001 MPa
Tensile yield strength, ST
Historical Public Release Table Value
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in; ST direction; applies from 2.001 through 4.000 in
434.37 MPa
Compressive yield strength, ST
Historical Public Release Table Value
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in; ST direction; applies from 2.001 through 4.000 in
|
| Tensile strength |
496.423 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in; L direction
496.423 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in; LT direction
468.843 MPa
Ultimate tensile strength, ST
Historical Public Release Table Value
7050-T7451; plate; 12.7-100 mm; lower A-basis value across 0.500-4.000 in; ST direction; applies from 2.001 through 4.000 in
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|