Compare candidate materials with unit-aware values and condition metadata.
| Property |
Aluminum 7050-T7452 hand forging, <=175 mm (MIL-HDBK-5H)
7050-T7452; hand forging; <=175 mm thickness at heat treatment | hand forging
|
|---|---|
| Density |
2823 kg/m^3
Density
Historical Nominal
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
70.327 GPa
Young's modulus
Historical Nominal
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in
|
| Shear modulus |
26.89 GPa
Shear modulus
Historical Nominal
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in
|
| Yield strength |
386.106 MPa
Tensile yield strength, L
Historical Public Release Table Value
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in; L direction
372.317 MPa
Tensile yield strength, LT
Historical Public Release Table Value
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in; LT direction
386.106 MPa
Compressive yield strength, L
Historical Public Release Table Value
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in; L direction
393.001 MPa
Compressive yield strength, LT
Historical Public Release Table Value
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in; LT direction
351.633 MPa
Tensile yield strength, ST
Historical Public Release Table Value
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in; ST direction; available from 2.001 in and above
386.106 MPa
Compressive yield strength, ST
Historical Public Release Table Value
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in; ST direction; available from 2.001 in and above
|
| Tensile strength |
468.843 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in; L direction
461.949 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in; LT direction
448.159 MPa
Ultimate tensile strength, ST
Historical Public Release Table Value
7050-T7452; hand forging; <=175 mm thickness at heat treatment; lower S/A-basis value across <=7.000 in; ST direction; available from 2.001 in and above
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|