Aluminum 7050-T76511 extrusion, <=50 mm (MIL-HDBK-5H)
7050-T76511; extrusion; <=50 mm thickness at quench | extrusion
|
|---|---|
| Density |
2823 kg/m^3
Density
Historical Nominal
7050-T76511; extrusion; <=50 mm thickness at quench; lower S/A-basis value across <=2.000 in, limited here to <=50 mm
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
71.016 GPa
Young's modulus
Historical Nominal
7050-T76511; extrusion; <=50 mm thickness at quench; lower S/A-basis value across <=2.000 in, limited here to <=50 mm
|
| Shear modulus |
26.89 GPa
Shear modulus
Historical Nominal
7050-T76511; extrusion; <=50 mm thickness at quench; lower S/A-basis value across <=2.000 in, limited here to <=50 mm
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7050-T76511; extrusion; <=50 mm thickness at quench; lower S/A-basis value across <=2.000 in, limited here to <=50 mm
|
| Yield strength |
468.843 MPa
Tensile yield strength, L
Historical Public Release Table Value
7050-T76511; extrusion; <=50 mm thickness at quench; lower S/A-basis value across <=2.000 in, limited here to <=50 mm; L direction
448.159 MPa
Tensile yield strength, LT
Historical Public Release Table Value
7050-T76511; extrusion; <=50 mm thickness at quench; lower S/A-basis value across <=2.000 in, limited here to <=50 mm; LT direction
468.843 MPa
Compressive yield strength, L
Historical Public Release Table Value
7050-T76511; extrusion; <=50 mm thickness at quench; lower S/A-basis value across <=2.000 in, limited here to <=50 mm; L direction
475.738 MPa
Compressive yield strength, LT
Historical Public Release Table Value
7050-T76511; extrusion; <=50 mm thickness at quench; lower S/A-basis value across <=2.000 in, limited here to <=50 mm; LT direction
|
| Tensile strength |
530.896 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7050-T76511; extrusion; <=50 mm thickness at quench; lower S/A-basis value across <=2.000 in, limited here to <=50 mm; L direction
517.107 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
7050-T76511; extrusion; <=50 mm thickness at quench; lower S/A-basis value across <=2.000 in, limited here to <=50 mm; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|