| Property |
Aluminum 7149-T73 die forging, <=100 mm (MIL-HDBK-5H)
7149-T73; die forging; <=100 mm thickness at heat treatment | die forging
|
|---|---|
| Density |
2851 kg/m^3
Density
Historical Nominal
7149-T73; die forging; <=100 mm thickness at heat treatment; lower A-basis value across <=4.000 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
70.327 GPa
Young's modulus
Historical Nominal
7149-T73; die forging; <=100 mm thickness at heat treatment; lower A-basis value across <=4.000 in
|
| Shear modulus |
26.89 GPa
Shear modulus
Historical Nominal
7149-T73; die forging; <=100 mm thickness at heat treatment; lower A-basis value across <=4.000 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7149-T73; die forging; <=100 mm thickness at heat treatment; lower A-basis value across <=4.000 in
|
| Yield strength |
393.001 MPa
Tensile yield strength, L
Historical Public Release Table Value
7149-T73; die forging; <=100 mm thickness at heat treatment; lower A-basis value across <=4.000 in; L direction
406.791 MPa
Compressive yield strength, L
Historical Public Release Table Value
7149-T73; die forging; <=100 mm thickness at heat treatment; lower A-basis value across <=4.000 in; L direction
413.685 MPa
Tensile yield strength, T
Historical Public Release Table Value
7149-T73; die forging; <=100 mm thickness at heat treatment; lower A-basis value across <=4.000 in; T direction
365.422 MPa
Compressive yield strength, ST
Historical Public Release Table Value
7149-T73; die forging; <=100 mm thickness at heat treatment; lower A-basis value across <=4.000 in; ST direction
|
| Tensile strength |
468.843 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7149-T73; die forging; <=100 mm thickness at heat treatment; lower A-basis value across <=4.000 in; L direction
482.633 MPa
Ultimate tensile strength, T
Historical Public Release Table Value
7149-T73; die forging; <=100 mm thickness at heat treatment; lower A-basis value across <=4.000 in; T direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|