| Property |
Aluminum 7150-T7751 plate, 9-42.5 mm (MIL-HDBK-5H)
7150-T7751; plate; 9-42.5 mm | plate
|
|---|---|
| Density |
2823 kg/m^3
Density
Historical Nominal
7150-T7751; plate; 9-42.5 mm; lower S-basis value across 0.354-1.673 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
71.016 GPa
Young's modulus
Historical Nominal
7150-T7751; plate; 9-42.5 mm; lower S-basis value across 0.354-1.673 in
|
| Shear modulus |
26.89 GPa
Shear modulus
Historical Nominal
7150-T7751; plate; 9-42.5 mm; lower S-basis value across 0.354-1.673 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7150-T7751; plate; 9-42.5 mm; lower S-basis value across 0.354-1.673 in
|
| Yield strength |
510.212 MPa
Tensile yield strength, L
Historical Public Release Table Value
7150-T7751; plate; 9-42.5 mm; lower S-basis value across 0.354-1.673 in; L direction
510.212 MPa
Tensile yield strength, LT
Historical Public Release Table Value
7150-T7751; plate; 9-42.5 mm; lower S-basis value across 0.354-1.673 in; LT direction
510.212 MPa
Compressive yield strength, L
Historical Public Release Table Value
7150-T7751; plate; 9-42.5 mm; lower S-basis value across 0.354-1.673 in; L direction
530.896 MPa
Compressive yield strength, LT
Historical Public Release Table Value
7150-T7751; plate; 9-42.5 mm; lower S-basis value across 0.354-1.673 in; LT direction
|
| Tensile strength |
551.581 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7150-T7751; plate; 9-42.5 mm; lower S-basis value across 0.354-1.673 in; L direction
551.581 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
7150-T7751; plate; 9-42.5 mm; lower S-basis value across 0.354-1.673 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|