| Property |
Aluminum 7150-T77511 extrusion, 18-29 mm (MIL-HDBK-5H)
7150-T77511; extrusion; 18-29 mm thickness at quench | extrusion
|
|---|---|
| Density |
2823 kg/m^3
Density
Historical Nominal
7150-T77511; extrusion; 18-29 mm thickness at quench; lower S-basis value across 0.709-1.142 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
71.705 GPa
Young's modulus
Historical Nominal
7150-T77511; extrusion; 18-29 mm thickness at quench; lower S-basis value across 0.709-1.142 in
|
| Shear modulus |
27.579 GPa
Shear modulus
Historical Nominal
7150-T77511; extrusion; 18-29 mm thickness at quench; lower S-basis value across 0.709-1.142 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7150-T77511; extrusion; 18-29 mm thickness at quench; lower S-basis value across 0.709-1.142 in
|
| Yield strength |
572.265 MPa
Tensile yield strength, L
Historical Public Release Table Value
7150-T77511; extrusion; 18-29 mm thickness at quench; lower S-basis value across 0.709-1.142 in; L direction
537.791 MPa
Tensile yield strength, LT
Historical Public Release Table Value
7150-T77511; extrusion; 18-29 mm thickness at quench; lower S-basis value across 0.709-1.142 in; LT direction
572.265 MPa
Compressive yield strength, L
Historical Public Release Table Value
7150-T77511; extrusion; 18-29 mm thickness at quench; lower S-basis value across 0.709-1.142 in; L direction
558.475 MPa
Compressive yield strength, LT
Historical Public Release Table Value
7150-T77511; extrusion; 18-29 mm thickness at quench; lower S-basis value across 0.709-1.142 in; LT direction
|
| Tensile strength |
606.739 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7150-T77511; extrusion; 18-29 mm thickness at quench; lower S-basis value across 0.709-1.142 in; L direction
572.265 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
7150-T77511; extrusion; 18-29 mm thickness at quench; lower S-basis value across 0.709-1.142 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|