Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Aluminum 7175-T74 hand forging, 25.4-100 mm (MIL-HDBK-5H)
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment | hand forging
|
|---|---|
| Density |
2796 kg/m^3
Density
Historical Nominal
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
70.327 GPa
Young's modulus
Historical Nominal
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in
|
| Shear modulus |
26.89 GPa
Shear modulus
Historical Nominal
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in
|
| Yield strength |
420.58 MPa
Tensile yield strength, L
Historical Public Release Table Value
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in; L direction
399.896 MPa
Tensile yield strength, LT
Historical Public Release Table Value
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in; LT direction
420.58 MPa
Compressive yield strength, L
Historical Public Release Table Value
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in; L direction
420.58 MPa
Compressive yield strength, LT
Historical Public Release Table Value
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in; LT direction
393.001 MPa
Tensile yield strength, ST
Historical Public Release Table Value
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in; ST direction; available from 2.001 in
413.685 MPa
Compressive yield strength, ST
Historical Public Release Table Value
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in; ST direction; available from 1.001 in
|
| Tensile strength |
489.528 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in; L direction
482.633 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in; LT direction
468.843 MPa
Ultimate tensile strength, ST
Historical Public Release Table Value
7175-T74; hand forging; 25.4-100 mm thickness at heat treatment; lower S-basis value across 1.001-4.000 in; ST direction; available from 2.001 in
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|