| Property |
9Ni-4Co-0.20C quenched-and-tempered plate (MIL-HDBK-5H)
9Ni-4Co-0.20C; quenched and tempered; plate; <203.2 mm | plate
|
|---|---|
| Density |
7833 kg/m^3
Density
Historical Nominal
9Ni-4Co-0.20C; quenched and tempered; plate; <203.2 mm; S-basis; lower elongation across the two listed thickness columns
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
198.569 GPa
Young's modulus
Historical Nominal
9Ni-4Co-0.20C; quenched and tempered; plate; <203.2 mm; S-basis; lower elongation across the two listed thickness columns
|
| Shear modulus |
76.532 GPa
Shear modulus
Historical Nominal
9Ni-4Co-0.20C; quenched and tempered; plate; <203.2 mm; S-basis; lower elongation across the two listed thickness columns
|
| Poisson's ratio |
0.3 -
Poisson's ratio
Historical Nominal
9Ni-4Co-0.20C; quenched and tempered; plate; <203.2 mm; S-basis; lower elongation across the two listed thickness columns
|
| Yield strength |
1192.793 MPa
Tensile yield strength, L
Historical Public Release Table Value
9Ni-4Co-0.20C; quenched and tempered; plate; <203.2 mm; S-basis; lower elongation across the two listed thickness columns; L direction
1206.583 MPa
Tensile yield strength, LT
Historical Public Release Table Value
9Ni-4Co-0.20C; quenched and tempered; plate; <203.2 mm; S-basis; lower elongation across the two listed thickness columns; LT direction
1296.214 MPa
Compressive yield strength, L
Historical Public Release Table Value
9Ni-4Co-0.20C; quenched and tempered; plate; <203.2 mm; S-basis; lower elongation across the two listed thickness columns; L direction
1289.32 MPa
Compressive yield strength, LT
Historical Public Release Table Value
9Ni-4Co-0.20C; quenched and tempered; plate; <203.2 mm; S-basis; lower elongation across the two listed thickness columns; LT direction
|
| Tensile strength |
1282.425 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
9Ni-4Co-0.20C; quenched and tempered; plate; <203.2 mm; S-basis; lower elongation across the two listed thickness columns; L direction
1310.004 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
9Ni-4Co-0.20C; quenched and tempered; plate; <203.2 mm; S-basis; lower elongation across the two listed thickness columns; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|