Alloy 188 solution-treated sheet, <4.75 mm (MIL-HDBK-5H)
Alloy 188; solution treated; sheet; <4.75 mm | sheet
|
|---|---|
| Density |
8968 kg/m^3
Density
Historical Nominal
Alloy 188; solution treated; sheet; <4.75 mm; S-basis lower value across <0.020 and 0.020-0.187 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
231.664 GPa
Young's modulus
Historical Nominal
Alloy 188; solution treated; sheet; <4.75 mm; S-basis lower value across <0.020 and 0.020-0.187 in
|
| Shear modulus |
88.253 GPa
Shear modulus
Historical Nominal
Alloy 188; solution treated; sheet; <4.75 mm; S-basis lower value across <0.020 and 0.020-0.187 in
|
| Poisson's ratio |
0.31 -
Poisson's ratio
Historical Nominal
Alloy 188; solution treated; sheet; <4.75 mm; S-basis lower value across <0.020 and 0.020-0.187 in
|
| Yield strength |
393.001 MPa
Tensile yield strength, L
Historical Public Release Table Value
Alloy 188; solution treated; sheet; <4.75 mm; S-basis lower value across <0.020 and 0.020-0.187 in; L direction
379.212 MPa
Tensile yield strength, LT
Historical Public Release Table Value
Alloy 188; solution treated; sheet; <4.75 mm; S-basis lower value across <0.020 and 0.020-0.187 in; LT direction
379.212 MPa
Compressive yield strength, LT
Historical Public Release Table Value
Alloy 188; solution treated; sheet; <4.75 mm; S-basis lower value across <0.020 and 0.020-0.187 in; LT direction
|
| Tensile strength |
861.845 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
Alloy 188; solution treated; sheet; <4.75 mm; S-basis lower value across <0.020 and 0.020-0.187 in; L direction
861.845 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
Alloy 188; solution treated; sheet; <4.75 mm; S-basis lower value across <0.020 and 0.020-0.187 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|