| Property |
Aluminum D357.0-T6 casting, conservative area (MIL-HDBK-5H)
D357.0-T6; casting; location and acceptance class must be established | casting
|
|---|---|
| Density |
2685 kg/m^3
Density
Historical Nominal
D357.0-T6; casting; location and acceptance class must be established; S-basis nondesignated-area values
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
71.705 GPa
Young's modulus
Historical Nominal
D357.0-T6; casting; location and acceptance class must be established; S-basis nondesignated-area values
|
| Shear modulus |
26.89 GPa
Shear modulus
Historical Nominal
D357.0-T6; casting; location and acceptance class must be established; S-basis nondesignated-area values
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
D357.0-T6; casting; location and acceptance class must be established; S-basis nondesignated-area values
|
| Yield strength |
248.211 MPa
Tensile yield strength
Historical Public Release Table Value
D357.0-T6; casting; location and acceptance class must be established; S-basis nondesignated-area values
248.211 MPa
Compressive yield strength
Historical Public Release Table Value
D357.0-T6; casting; location and acceptance class must be established; S-basis nondesignated-area values
|
| Tensile strength |
310.264 MPa
Ultimate tensile strength
Historical Public Release Table Value
D357.0-T6; casting; location and acceptance class must be established; S-basis nondesignated-area values
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|