Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Ti-10V-2Fe-3Al STA die forging, <76.2 mm (MIL-HDBK-5H)
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm | conventional die forging
|
|---|---|
| Density |
4650 kg/m^3
Density
Historical Nominal
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm; S-basis, AMS 4984 <3.000 in column
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
109.627 GPa
Young's modulus
Historical Nominal
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm; S-basis, AMS 4984 <3.000 in column
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
1103.161 MPa
Tensile yield strength, L
Historical Public Release Table Value
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm; S-basis, AMS 4984 <3.000 in column; L direction
1103.161 MPa
Tensile yield strength, LT
Historical Public Release Table Value
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm; S-basis, AMS 4984 <3.000 in column; LT direction
1158.319 MPa
Compressive yield strength, L
Historical Public Release Table Value
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm; S-basis, AMS 4984 <3.000 in column; L direction
1144.53 MPa
Compressive yield strength, LT
Historical Public Release Table Value
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm; S-basis, AMS 4984 <3.000 in column; LT direction
1103.161 MPa
Tensile yield strength, ST
Historical Public Release Table Value
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm; S-basis, AMS 4984 <3.000 in column; ST direction
1144.53 MPa
Compressive yield strength, ST
Historical Public Release Table Value
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm; S-basis, AMS 4984 <3.000 in column; ST direction
|
| Tensile strength |
1192.793 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm; S-basis, AMS 4984 <3.000 in column; L direction
1192.793 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm; S-basis, AMS 4984 <3.000 in column; LT direction
1192.793 MPa
Ultimate tensile strength, ST
Historical Public Release Table Value
Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm; S-basis, AMS 4984 <3.000 in column; ST direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|