Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
AA6261 remelted/stir-cast base control (CC BY research instance)
AA6261 source-labeled present alloy and remelted/stir-cast unreinforced base control | laboratory remelted/stir-cast base-control tensile and hardness specimens
|
|---|---|
| Density |
2710.0 kg/m^3
Density
Source Reported Present Value Screening
source-labeled present 6261 AA row; measurement method, specimen state and its exact relationship to the subsequently remelted base-control specimens are not stated
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
78.0 GPa
Young's modulus
Source Reported Present Value Screening
source-labeled present 6261 AA row; measurement method, specimen state and its exact relationship to the subsequently remelted base-control specimens are not stated
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
98.0 MPa
Yield strength (Table 2 present row)
Source Reported Present Value Screening
source-labeled present 6261 AA row; measurement method, specimen state and its exact relationship to the subsequently remelted base-control specimens are not stated
151.0 MPa
Tensile yield strength
Experimental Measured Screening
source-labeled AA base-control row after shredding/remelting and stir casting at 1123 K; 500 g AA with no SiC or ZrO2 addition; no temper, prior product form, heat treatment, tensile direction, heat/batch identity or population statistic is stated; tensile test reported at 28 degC and 45% moisture
|
| Tensile strength |
160.0 MPa
Ultimate tensile strength
Experimental Measured Screening
source-labeled AA base-control row after shredding/remelting and stir casting at 1123 K; 500 g AA with no SiC or ZrO2 addition; no temper, prior product form, heat treatment, tensile direction, heat/batch identity or population statistic is stated; tensile test reported at 28 degC and 45% moisture
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|