Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
AA6008-T7 hollow extrusion, patent example A1 (patent overheat-and-cool route)
AA6008-T7 patent-example hollow profile A1 | mono-chamber rectangular hollow extruded profile
|
|---|---|
| Density |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
288.0 MPa
Tensile yield strength
Experimental Measured Screening
patent example Alloy A / profile A1, explicitly AA6008-T7; mono-chamber hollow extrusion approximately 40 x 55 mm with wall thickness close to 2.5 mm; tensile-specimen orientation and test temperature not stated
|
| Tensile strength |
301.0 MPa
Ultimate tensile strength
Experimental Measured Screening
patent example Alloy A / profile A1, explicitly AA6008-T7; mono-chamber hollow extrusion approximately 40 x 55 mm with wall thickness close to 2.5 mm; tensile-specimen orientation and test temperature not stated
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|