| Property |
AA6008-T6 hollow extrusion, patent example A3 (conventional 170 degC ageing route)
AA6008-T6 patent-example hollow profile A3 | mono-chamber rectangular hollow extruded profile
|
|---|---|
| Density |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
277.0 MPa
Tensile yield strength
Experimental Measured Screening
patent example Alloy A / profile A3, explicitly AA6008-T6; mono-chamber hollow extrusion approximately 40 x 55 mm with wall thickness close to 2.5 mm; tensile-specimen orientation and test temperature not stated
|
| Tensile strength |
296.0 MPa
Ultimate tensile strength
Experimental Measured Screening
patent example Alloy A / profile A3, explicitly AA6008-T6; mono-chamber hollow extrusion approximately 40 x 55 mm with wall thickness close to 2.5 mm; tensile-specimen orientation and test temperature not stated
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|