EN AW-2618A-T61 forging, overaged 1000 h at 230 degC (CC BY experimental)
EN AW-2618A forged cylindrical blank, initially T61, then overaged 1000 h at 230 degC and air cooled | forged cylindrical blank; semi-finished stock for radial compressor wheels
|
|---|---|
| Density |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
265.0 MPa
Tensile yield strength
Reported Ccby Experimental Screening
EN AW-2618A forged blank, T61 plus 1000 h at 230 degC overageing; rectangular blocks 16 x 16 x 100 mm extracted from section 3; one tensile test per temperature; room temperature
181.0 MPa
Tensile yield strength at 230 degC
Reported Ccby Experimental Screening
EN AW-2618A forged blank, T61 plus 1000 h at 230 degC overageing; rectangular blocks 16 x 16 x 100 mm extracted from section 3; one tensile test per temperature; test temperature 230 degC
|
| Tensile strength |
351.0 MPa
Ultimate tensile strength
Reported Ccby Experimental Screening
EN AW-2618A forged blank, T61 plus 1000 h at 230 degC overageing; rectangular blocks 16 x 16 x 100 mm extracted from section 3; one tensile test per temperature; room temperature
191.0 MPa
Ultimate tensile strength at 230 degC
Reported Ccby Experimental Screening
EN AW-2618A forged blank, T61 plus 1000 h at 230 degC overageing; rectangular blocks 16 x 16 x 100 mm extracted from section 3; one tensile test per temperature; test temperature 230 degC
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|