Aluminum 2014-T6/T651 bar and rod, <=75 mm (MIL-HDBK-5H)
2014-T6/T651; bar or rod; <=75 mm | rolled, drawn, or cold-finished bar or rod
|
|---|---|
| Density |
2796 kg/m^3
Density
Historical Nominal
2014-T6/T651; bar or rod; <=75 mm; S-basis lower value across <=3.000 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
72.395 GPa
Young's modulus
Historical Nominal
2014-T6/T651; bar or rod; <=75 mm; S-basis lower value across <=3.000 in
|
| Shear modulus |
27.579 GPa
Shear modulus
Historical Nominal
2014-T6/T651; bar or rod; <=75 mm; S-basis lower value across <=3.000 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
2014-T6/T651; bar or rod; <=75 mm; S-basis lower value across <=3.000 in
|
| Yield strength |
379.212 MPa
Tensile yield strength, L
Historical Public Release Table Value
2014-T6/T651; bar or rod; <=75 mm; S-basis lower value across <=3.000 in; L direction
351.633 MPa
Tensile yield strength, LT
Historical Public Release Table Value
2014-T6/T651; bar or rod; <=75 mm; S-basis lower value across <=3.000 in; LT direction
365.422 MPa
Compressive yield strength, L
Historical Public Release Table Value
2014-T6/T651; bar or rod; <=75 mm; S-basis lower value across <=3.000 in; L direction
|
| Tensile strength |
448.159 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
2014-T6/T651; bar or rod; <=75 mm; S-basis lower value across <=3.000 in; L direction
427.475 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
2014-T6/T651; bar or rod; <=75 mm; S-basis lower value across <=3.000 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|