Metal
Aluminum 2014-T6/T651 bar and rod, <=75 mm (MIL-HDBK-5H)
Historical public-release S-basis bar/rod reference conservatively combined through 75 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2796 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 448.159 | MPa |
| Tensile yield strength, L | 379.212 | MPa |
| Ultimate tensile strength, LT | 427.475 | MPa |
| Tensile yield strength, LT | 351.633 | MPa |
| Compressive yield strength, L | 365.422 | MPa |
| Ultimate shear strength | 262.001 | MPa |
| Elongation, L | 8 | % |
| Young's modulus | 72.395 | GPa |
| Compression modulus | 73.774 | GPa |
| Shear modulus | 27.579 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 2014-T6/T651; bar or rod; <=75 mm
- Temper
- T6 or T651
- Heat treatment
- solution heat treated and artificially aged
- Product form
- rolled, drawn, or cold-finished bar or rod
- Thickness / diameter range
- <=2.953 in (75 mm), within the handbook's <=3.000 in bands
- Test direction
- L and LT; lower listed value across size bands
- Processing route
- wrought heat-treatable aluminum bar or rod
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.