Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Aluminum 2014-T652 hand forging, 50-75 mm (MIL-HDBK-5H)
2014-T652; hand forging; 50-75 mm thickness at heat treatment | hand forging
|
|---|---|
| Density |
2796 kg/m^3
Density
Historical Nominal
2014-T652; hand forging; 50-75 mm thickness at heat treatment; S-basis lower value across <=2.000 and 2.001-3.000 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
72.395 GPa
Young's modulus
Historical Nominal
2014-T652; hand forging; 50-75 mm thickness at heat treatment; S-basis lower value across <=2.000 and 2.001-3.000 in
|
| Shear modulus |
27.579 GPa
Shear modulus
Historical Nominal
2014-T652; hand forging; 50-75 mm thickness at heat treatment; S-basis lower value across <=2.000 and 2.001-3.000 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
2014-T652; hand forging; 50-75 mm thickness at heat treatment; S-basis lower value across <=2.000 and 2.001-3.000 in
|
| Yield strength |
386.106 MPa
Tensile yield strength, L
Historical Public Release Table Value
2014-T652; hand forging; 50-75 mm thickness at heat treatment; S-basis lower value across <=2.000 and 2.001-3.000 in; L direction
379.212 MPa
Tensile yield strength, LT
Historical Public Release Table Value
2014-T652; hand forging; 50-75 mm thickness at heat treatment; S-basis lower value across <=2.000 and 2.001-3.000 in; LT direction
386.106 MPa
Compressive yield strength, L
Historical Public Release Table Value
2014-T652; hand forging; 50-75 mm thickness at heat treatment; S-basis lower value across <=2.000 and 2.001-3.000 in; L direction
386.106 MPa
Compressive yield strength, LT
Historical Public Release Table Value
2014-T652; hand forging; 50-75 mm thickness at heat treatment; S-basis lower value across <=2.000 and 2.001-3.000 in; LT direction
|
| Tensile strength |
441.264 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
2014-T652; hand forging; 50-75 mm thickness at heat treatment; S-basis lower value across <=2.000 and 2.001-3.000 in; L direction
441.264 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
2014-T652; hand forging; 50-75 mm thickness at heat treatment; S-basis lower value across <=2.000 and 2.001-3.000 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|