Metal
Aluminum 2014-T652 hand forging, 50-75 mm (MIL-HDBK-5H)
Historical public-release S-basis hand-forging reference conservatively combined over 50-75 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2796 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 441.264 | MPa |
| Tensile yield strength, L | 386.106 | MPa |
| Ultimate tensile strength, LT | 441.264 | MPa |
| Tensile yield strength, LT | 379.212 | MPa |
| Compressive yield strength, L | 386.106 | MPa |
| Compressive yield strength, LT | 386.106 | MPa |
| Ultimate shear strength | 255.106 | MPa |
| Elongation, L | 8 | % |
| Elongation, LT | 3 | % |
| Young's modulus | 72.395 | GPa |
| Compression modulus | 74.463 | GPa |
| Shear modulus | 27.579 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 2014-T652; hand forging; 50-75 mm thickness at heat treatment
- Temper
- T652
- Heat treatment
- solution heat treated, stress relieved and artificially aged
- Product form
- hand forging
- Thickness / diameter range
- 1.969-2.953 in (50-75 mm), within the <=2.000 and 2.001-3.000 in bands
- Test direction
- L, LT and ST material axes; lower listed value across size bands
- Processing route
- hand-forged heat-treatable aluminum alloy
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI