Aluminum-lithium 2090-T83 sheet, 1.016-6.3 mm (MIL-HDBK-5H)
2090-T83; sheet; 1.016-6.3 mm | sheet
|
|---|---|
| Density |
2602 kg/m^3
Density
Historical Nominal
2090-T83; sheet; 1.016-6.3 mm; lower S-basis value across 0.040-0.249 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
79.29 GPa
Young's modulus
Historical Nominal
2090-T83; sheet; 1.016-6.3 mm; lower S-basis value across 0.040-0.249 in
|
| Shear modulus |
29.647 GPa
Shear modulus
Historical Nominal
2090-T83; sheet; 1.016-6.3 mm; lower S-basis value across 0.040-0.249 in
|
| Poisson's ratio |
0.34 -
Poisson's ratio
Historical Nominal
2090-T83; sheet; 1.016-6.3 mm; lower S-basis value across 0.040-0.249 in
|
| Yield strength |
482.633 MPa
Tensile yield strength, L
Historical Public Release Table Value
2090-T83; sheet; 1.016-6.3 mm; lower S-basis value across 0.040-0.249 in; L direction
455.054 MPa
Tensile yield strength, LT
Historical Public Release Table Value
2090-T83; sheet; 1.016-6.3 mm; lower S-basis value across 0.040-0.249 in; LT direction
434.37 MPa
Compressive yield strength, L
Historical Public Release Table Value
2090-T83; sheet; 1.016-6.3 mm; lower S-basis value across 0.040-0.249 in; L direction
489.528 MPa
Compressive yield strength, LT
Historical Public Release Table Value
2090-T83; sheet; 1.016-6.3 mm; lower S-basis value across 0.040-0.249 in; LT direction
|
| Tensile strength |
517.107 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
2090-T83; sheet; 1.016-6.3 mm; lower S-basis value across 0.040-0.249 in; L direction
503.317 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
2090-T83; sheet; 1.016-6.3 mm; lower S-basis value across 0.040-0.249 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|