Metal
Aluminum-lithium 2090-T83 sheet, 1.016-6.3 mm (MIL-HDBK-5H)
Historical public-release S-basis aluminum-lithium sheet reference.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2602 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 517.107 | MPa |
| Tensile yield strength, L | 482.633 | MPa |
| Ultimate tensile strength, LT | 503.317 | MPa |
| Tensile yield strength, LT | 455.054 | MPa |
| Compressive yield strength, L | 434.37 | MPa |
| Compressive yield strength, LT | 489.528 | MPa |
| Ultimate shear strength | 255.106 | MPa |
| Elongation, L | 3 | % |
| Elongation, LT | 5 | % |
| Ramberg-Osgood exponent, tension L | 14 | - |
| Ramberg-Osgood exponent, tension LT | 12 | - |
| Ramberg-Osgood exponent, compression L | 20 | - |
| Ramberg-Osgood exponent, compression LT | 19 | - |
| Young's modulus | 79.29 | GPa |
| Compression modulus | 81.358 | GPa |
| Shear modulus | 29.647 | GPa |
| Poisson's ratio | 0.34 | - |
Units
Condition
- Condition
- 2090-T83; sheet; 1.016-6.3 mm
- Temper
- T83
- Heat treatment
- solution heat treated, cold worked and artificially aged
- Product form
- sheet
- Thickness / diameter range
- 0.040-0.248 in (1.016-6.3 mm), within the 0.040-0.249 in table bands
- Test direction
- L and LT; lower listed value across applicable columns
- Processing route
- wrought heat-treatable aluminum-copper-lithium sheet
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI