| Property |
Aluminum 2219-T87 sheet/plate, 3.2-25 mm (MIL-HDBK-5H)
2219-T87; sheet or plate; 3.2-25 mm | sheet or plate
|
|---|---|
| Density |
2851 kg/m^3
Density
Historical Nominal
2219-T87; sheet or plate; 3.2-25 mm; lower A-basis value across sheet and plate tables
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
72.395 GPa
Young's modulus
Historical Nominal
2219-T87; sheet or plate; 3.2-25 mm; lower A-basis value across sheet and plate tables
|
| Shear modulus |
27.579 GPa
Shear modulus
Historical Nominal
2219-T87; sheet or plate; 3.2-25 mm; lower A-basis value across sheet and plate tables
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
2219-T87; sheet or plate; 3.2-25 mm; lower A-basis value across sheet and plate tables
|
| Yield strength |
344.738 MPa
Tensile yield strength, L
Historical Public Release Table Value
2219-T87; sheet or plate; 3.2-25 mm; lower A-basis value across sheet and plate tables; L direction
351.633 MPa
Tensile yield strength, LT
Historical Public Release Table Value
2219-T87; sheet or plate; 3.2-25 mm; lower A-basis value across sheet and plate tables; LT direction
351.633 MPa
Compressive yield strength, L
Historical Public Release Table Value
2219-T87; sheet or plate; 3.2-25 mm; lower A-basis value across sheet and plate tables; L direction
365.422 MPa
Compressive yield strength, LT
Historical Public Release Table Value
2219-T87; sheet or plate; 3.2-25 mm; lower A-basis value across sheet and plate tables; LT direction
|
| Tensile strength |
434.37 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
2219-T87; sheet or plate; 3.2-25 mm; lower A-basis value across sheet and plate tables; L direction
441.264 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
2219-T87; sheet or plate; 3.2-25 mm; lower A-basis value across sheet and plate tables; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|