Metal
Aluminum 2219-T87 sheet/plate, 3.2-25 mm (MIL-HDBK-5H)
Historical public-release A-basis 2219-T87 sheet and plate reference.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2851 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 434.37 | MPa |
| Tensile yield strength, L | 344.738 | MPa |
| Ultimate tensile strength, LT | 441.264 | MPa |
| Tensile yield strength, LT | 351.633 | MPa |
| Compressive yield strength, L | 351.633 | MPa |
| Compressive yield strength, LT | 365.422 | MPa |
| Ultimate shear strength | 248.211 | MPa |
| Elongation, LT | 5 | % |
| Ramberg-Osgood exponent, tension L | 14 | - |
| Ramberg-Osgood exponent, tension LT | 14 | - |
| Ramberg-Osgood exponent, compression L | 14 | - |
| Ramberg-Osgood exponent, compression LT | 14 | - |
| Young's modulus | 72.395 | GPa |
| Compression modulus | 74.463 | GPa |
| Shear modulus | 27.579 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 2219-T87; sheet or plate; 3.2-25 mm
- Temper
- T87
- Heat treatment
- solution heat treated, cold worked and artificially aged
- Product form
- sheet or plate
- Thickness / diameter range
- 0.126-0.984 in (3.2-25 mm), within the sheet/plate table bands
- Test direction
- L and LT
- Processing route
- wrought heat-treatable aluminum-copper sheet or plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.