Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Aluminum 5052-H32 sheet/plate (MIL-HDBK-5H)
5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm) | sheet and plate
|
|---|---|
| Density |
2685 kg/m^3
Density
Historical Nominal
5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm); Static values are from Table 3.5.1.0(b1); elongation is the lowest listed longitudinal value over this card's Table 3.5.1.0(b2) thickness range.
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
69.637 GPa
Young's modulus
Historical Nominal
5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm); Static values are from Table 3.5.1.0(b1); elongation is the lowest listed longitudinal value over this card's Table 3.5.1.0(b2) thickness range.
|
| Shear modulus |
26.545 GPa
Shear modulus
Historical Nominal
5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm); Static values are from Table 3.5.1.0(b1); elongation is the lowest listed longitudinal value over this card's Table 3.5.1.0(b2) thickness range.
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm); Static values are from Table 3.5.1.0(b1); elongation is the lowest listed longitudinal value over this card's Table 3.5.1.0(b2) thickness range.
|
| Yield strength |
158.579 MPa
Tensile yield strength, L
Historical Public Release Table Value
5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm); Static values are from Table 3.5.1.0(b1); elongation is the lowest listed longitudinal value over this card's Table 3.5.1.0(b2) thickness range.; L direction
151.685 MPa
Tensile yield strength, LT
Historical Public Release Table Value
5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm); Static values are from Table 3.5.1.0(b1); elongation is the lowest listed longitudinal value over this card's Table 3.5.1.0(b2) thickness range.; LT direction
151.685 MPa
Compressive yield strength, L
Historical Public Release Table Value
5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm); Static values are from Table 3.5.1.0(b1); elongation is the lowest listed longitudinal value over this card's Table 3.5.1.0(b2) thickness range.; L direction
158.579 MPa
Compressive yield strength, LT
Historical Public Release Table Value
5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm); Static values are from Table 3.5.1.0(b1); elongation is the lowest listed longitudinal value over this card's Table 3.5.1.0(b2) thickness range.; LT direction
|
| Tensile strength |
213.737 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm); Static values are from Table 3.5.1.0(b1); elongation is the lowest listed longitudinal value over this card's Table 3.5.1.0(b2) thickness range.; L direction
213.737 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm); Static values are from Table 3.5.1.0(b1); elongation is the lowest listed longitudinal value over this card's Table 3.5.1.0(b2) thickness range.; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|