Aluminum 5052-H32 sheet/plate (MIL-HDBK-5H)
Historical public-release S-basis 5052-H32 sheet/plate reference.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2685 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 213.737 | MPa |
| Tensile yield strength, L | 158.579 | MPa |
| Ultimate tensile strength, LT | 213.737 | MPa |
| Tensile yield strength, LT | 151.685 | MPa |
| Compressive yield strength, L | 151.685 | MPa |
| Compressive yield strength, LT | 158.579 | MPa |
| Ultimate shear strength | 131.0 | MPa |
| Elongation, L | 4 | % |
| Young's modulus | 69.637 | GPa |
| Compression modulus | 70.327 | GPa |
| Shear modulus | 26.545 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 5052-H32; sheet/plate; 0.017-2.000 in (0.432-50.8 mm)
- Temper
- H32
- Heat treatment
- strain hardened to H32
- Product form
- sheet and plate
- Thickness / diameter range
- 0.017-2.000 in (0.432-50.8 mm)
- Test direction
- L and LT where listed; elongation L
- Processing route
- wrought non-heat-treatable aluminum-magnesium sheet/plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.