Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Aluminum 7050-T74 die forging, <=75 mm (MIL-HDBK-5H)
7050-T74; die forging; <=75 mm thickness at heat treatment | die forging
|
|---|---|
| Density |
2823 kg/m^3
Density
Historical Nominal
7050-T74; die forging; <=75 mm thickness at heat treatment; S-basis lower value across <=4.000 in, limited here to <=75 mm
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
70.327 GPa
Young's modulus
Historical Nominal
7050-T74; die forging; <=75 mm thickness at heat treatment; S-basis lower value across <=4.000 in, limited here to <=75 mm
|
| Shear modulus |
26.89 GPa
Shear modulus
Historical Nominal
7050-T74; die forging; <=75 mm thickness at heat treatment; S-basis lower value across <=4.000 in, limited here to <=75 mm
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7050-T74; die forging; <=75 mm thickness at heat treatment; S-basis lower value across <=4.000 in, limited here to <=75 mm
|
| Yield strength |
420.58 MPa
Tensile yield strength, L
Historical Public Release Table Value
7050-T74; die forging; <=75 mm thickness at heat treatment; S-basis lower value across <=4.000 in, limited here to <=75 mm; L direction
434.37 MPa
Compressive yield strength, L
Historical Public Release Table Value
7050-T74; die forging; <=75 mm thickness at heat treatment; S-basis lower value across <=4.000 in, limited here to <=75 mm; L direction
379.212 MPa
Tensile yield strength, T
Historical Public Release Table Value
7050-T74; die forging; <=75 mm thickness at heat treatment; S-basis lower value across <=4.000 in, limited here to <=75 mm; T direction
406.791 MPa
Compressive yield strength, T
Historical Public Release Table Value
7050-T74; die forging; <=75 mm thickness at heat treatment; S-basis lower value across <=4.000 in, limited here to <=75 mm; T direction; handbook footnote states transverse Fcy is based on the ST direction
|
| Tensile strength |
489.528 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7050-T74; die forging; <=75 mm thickness at heat treatment; S-basis lower value across <=4.000 in, limited here to <=75 mm; L direction
461.949 MPa
Ultimate tensile strength, T
Historical Public Release Table Value
7050-T74; die forging; <=75 mm thickness at heat treatment; S-basis lower value across <=4.000 in, limited here to <=75 mm; T direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|