Metal
Aluminum 7050-T74 die forging, <=75 mm (MIL-HDBK-5H)
Historical public-release S-basis die-forging reference through 75 mm heat-treatment thickness.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2823 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 489.528 | MPa |
| Tensile yield strength, L | 420.58 | MPa |
| Compressive yield strength, L | 434.37 | MPa |
| Ultimate shear strength | 289.58 | MPa |
| Elongation, L | 7 | % |
| Ultimate tensile strength, T | 461.949 | MPa |
| Tensile yield strength, T | 379.212 | MPa |
| Compressive yield strength, T | 406.791 | MPa |
| Elongation, T | 4 | % |
| Ramberg-Osgood exponent, tension L | 11 | - |
| Ramberg-Osgood exponent, tension ST | 7.3 | - |
| Ramberg-Osgood exponent, compression L | 12 | - |
| Ramberg-Osgood exponent, compression ST | 18 | - |
| Young's modulus | 70.327 | GPa |
| Compression modulus | 73.774 | GPa |
| Shear modulus | 26.89 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 7050-T74; die forging; <=75 mm thickness at heat treatment
- Temper
- T74
- Heat treatment
- solution heat treated and overaged to T74 by the supplier
- Product form
- die forging
- Thickness / diameter range
- <=2.953 in (75 mm), within the <=4.000 in table bands
- Test direction
- L and transverse-to-flow directions; lower listed value across applicable size bands
- Processing route
- die-forged heat-treatable aluminum-zinc alloy
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.