Aluminum 7075-T73510/T73511 extrusion, 12.7-19 mm (MIL-HDBK-5H)
7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench | extruded rod, bar or shape
|
|---|---|
| Density |
2796 kg/m^3
Density
Historical Nominal
7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench; A-basis, 0.500-0.749 in table column
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
71.705 GPa
Young's modulus
Historical Nominal
7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench; A-basis, 0.500-0.749 in table column
|
| Shear modulus |
27.579 GPa
Shear modulus
Historical Nominal
7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench; A-basis, 0.500-0.749 in table column
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench; A-basis, 0.500-0.749 in table column
|
| Yield strength |
413.685 MPa
Tensile yield strength, L
Historical Public Release Table Value
7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench; A-basis, 0.500-0.749 in table column; L direction
393.001 MPa
Tensile yield strength, LT
Historical Public Release Table Value
7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench; A-basis, 0.500-0.749 in table column; LT direction
413.685 MPa
Compressive yield strength, L
Historical Public Release Table Value
7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench; A-basis, 0.500-0.749 in table column; L direction
413.685 MPa
Compressive yield strength, LT
Historical Public Release Table Value
7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench; A-basis, 0.500-0.749 in table column; LT direction
|
| Tensile strength |
482.633 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench; A-basis, 0.500-0.749 in table column; L direction
461.949 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench; A-basis, 0.500-0.749 in table column; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|