Aluminum 7075-T73510/T73511 extrusion, 12.7-19 mm (MIL-HDBK-5H)
Historical public-release A-basis overaged extrusion reference for 12.7-19 mm quench thickness.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2796 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 482.633 | MPa |
| Tensile yield strength, L | 413.685 | MPa |
| Ultimate tensile strength, LT | 461.949 | MPa |
| Tensile yield strength, LT | 393.001 | MPa |
| Compressive yield strength, L | 413.685 | MPa |
| Compressive yield strength, LT | 413.685 | MPa |
| Ultimate shear strength | 262.001 | MPa |
| Elongation, L | 8 | % |
| Ramberg-Osgood exponent, tension L | 34 | - |
| Ramberg-Osgood exponent, tension LT | 25 | - |
| Ramberg-Osgood exponent, compression L | 28 | - |
| Ramberg-Osgood exponent, compression LT | 28 | - |
| Young's modulus | 71.705 | GPa |
| Compression modulus | 73.774 | GPa |
| Shear modulus | 27.579 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 7075-T73510/T73511; extrusion; 12.7-19 mm thickness at quench
- Temper
- T73510 or T73511
- Heat treatment
- solution heat treated, stress relieved by stretching and overaged to T73 corrosion-resistant condition
- Product form
- extruded rod, bar or shape
- Thickness / diameter range
- 0.500-0.748 in (12.7-19 mm), within the 0.500-0.749 in table column
- Test direction
- L and LT
- Processing route
- wrought heat-treatable aluminum extrusion
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.