Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Aluminum 7150-T61511 extrusion, 20.32-50.8 mm (MIL-HDBK-5H)
7150-T61511; extrusion; 20.32-50.8 mm thickness at quench | extrusion
|
|---|---|
| Density |
2823 kg/m^3
Density
Historical Nominal
7150-T61511; extrusion; 20.32-50.8 mm thickness at quench; lower S/A-basis value across 0.800-2.000 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
71.705 GPa
Young's modulus
Historical Nominal
7150-T61511; extrusion; 20.32-50.8 mm thickness at quench; lower S/A-basis value across 0.800-2.000 in
|
| Shear modulus |
27.579 GPa
Shear modulus
Historical Nominal
7150-T61511; extrusion; 20.32-50.8 mm thickness at quench; lower S/A-basis value across 0.800-2.000 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7150-T61511; extrusion; 20.32-50.8 mm thickness at quench; lower S/A-basis value across 0.800-2.000 in
|
| Yield strength |
572.265 MPa
Tensile yield strength, L
Historical Public Release Table Value
7150-T61511; extrusion; 20.32-50.8 mm thickness at quench; lower S/A-basis value across 0.800-2.000 in; L direction
468.843 MPa
Tensile yield strength, LT
Historical Public Release Table Value
7150-T61511; extrusion; 20.32-50.8 mm thickness at quench; lower S/A-basis value across 0.800-2.000 in; LT direction
565.37 MPa
Compressive yield strength, L
Historical Public Release Table Value
7150-T61511; extrusion; 20.32-50.8 mm thickness at quench; lower S/A-basis value across 0.800-2.000 in; L direction
517.107 MPa
Compressive yield strength, LT
Historical Public Release Table Value
7150-T61511; extrusion; 20.32-50.8 mm thickness at quench; lower S/A-basis value across 0.800-2.000 in; LT direction
|
| Tensile strength |
613.633 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7150-T61511; extrusion; 20.32-50.8 mm thickness at quench; lower S/A-basis value across 0.800-2.000 in; L direction
510.212 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
7150-T61511; extrusion; 20.32-50.8 mm thickness at quench; lower S/A-basis value across 0.800-2.000 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|