Metal
Aluminum 7150-T61511 extrusion, 20.32-50.8 mm (MIL-HDBK-5H)
Historical public-release T61511 extrusion reference over the handbook's static-table range.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2823 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 613.633 | MPa |
| Tensile yield strength, L | 572.265 | MPa |
| Ultimate tensile strength, LT | 510.212 | MPa |
| Tensile yield strength, LT | 468.843 | MPa |
| Compressive yield strength, L | 565.37 | MPa |
| Compressive yield strength, LT | 517.107 | MPa |
| Ultimate shear strength | 289.58 | MPa |
| Elongation, L | 8 | % |
| Ramberg-Osgood exponent, tension L | 9.5 | - |
| Ramberg-Osgood exponent, tension LT | 9.5 | - |
| Ramberg-Osgood exponent, compression L | 16 | - |
| Ramberg-Osgood exponent, compression LT | 27 | - |
| Young's modulus | 71.705 | GPa |
| Compression modulus | 75.842 | GPa |
| Shear modulus | 27.579 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 7150-T61511; extrusion; 20.32-50.8 mm thickness at quench
- Temper
- T61511
- Heat treatment
- solution heat treated, stress relieved by stretching and artificially aged to the T61-type condition
- Product form
- extrusion
- Thickness / diameter range
- 0.800-2.000 in (20.32-50.8 mm); Ramberg-Osgood figures extend to 2.750 in
- Test direction
- L and LT; lower listed value across applicable columns
- Processing route
- wrought heat-treatable aluminum-zinc extrusion
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI