Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Aluminum 7475-T761 sheet, 1.016-6.3 mm (MIL-HDBK-5H)
7475-T761; bare sheet; 1.016-6.3 mm | bare sheet
|
|---|---|
| Density |
2796 kg/m^3
Density
Historical Nominal
7475-T761; bare sheet; 1.016-6.3 mm; lower A/S-basis value across 0.040-0.249 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
68.948 GPa
Young's modulus
Historical Nominal
7475-T761; bare sheet; 1.016-6.3 mm; lower A/S-basis value across 0.040-0.249 in
|
| Shear modulus |
26.2 GPa
Shear modulus
Historical Nominal
7475-T761; bare sheet; 1.016-6.3 mm; lower A/S-basis value across 0.040-0.249 in
|
| Poisson's ratio |
0.33 -
Poisson's ratio
Historical Nominal
7475-T761; bare sheet; 1.016-6.3 mm; lower A/S-basis value across 0.040-0.249 in
|
| Yield strength |
386.106 MPa
Tensile yield strength, L
Historical Public Release Table Value
7475-T761; bare sheet; 1.016-6.3 mm; lower A/S-basis value across 0.040-0.249 in; L direction
379.212 MPa
Tensile yield strength, LT
Historical Public Release Table Value
7475-T761; bare sheet; 1.016-6.3 mm; lower A/S-basis value across 0.040-0.249 in; LT direction
379.212 MPa
Compressive yield strength, L
Historical Public Release Table Value
7475-T761; bare sheet; 1.016-6.3 mm; lower A/S-basis value across 0.040-0.249 in; L direction
399.896 MPa
Compressive yield strength, LT
Historical Public Release Table Value
7475-T761; bare sheet; 1.016-6.3 mm; lower A/S-basis value across 0.040-0.249 in; LT direction
|
| Tensile strength |
455.054 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
7475-T761; bare sheet; 1.016-6.3 mm; lower A/S-basis value across 0.040-0.249 in; L direction
455.054 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
7475-T761; bare sheet; 1.016-6.3 mm; lower A/S-basis value across 0.040-0.249 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|