Metal
Aluminum 7475-T761 sheet, 1.016-6.3 mm (MIL-HDBK-5H)
Historical public-release 7475-T761 bare-sheet reference.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2796 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 455.054 | MPa |
| Tensile yield strength, L | 386.106 | MPa |
| Ultimate tensile strength, LT | 455.054 | MPa |
| Tensile yield strength, LT | 379.212 | MPa |
| Compressive yield strength, L | 379.212 | MPa |
| Compressive yield strength, LT | 399.896 | MPa |
| Ultimate shear strength | 275.79 | MPa |
| Elongation, LT | 9 | % |
| Ramberg-Osgood exponent, tension L | 26 | - |
| Ramberg-Osgood exponent, tension LT | 16 | - |
| Ramberg-Osgood exponent, compression L | 15 | - |
| Ramberg-Osgood exponent, compression LT | 19 | - |
| Young's modulus | 68.948 | GPa |
| Compression modulus | 72.395 | GPa |
| Shear modulus | 26.2 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 7475-T761; bare sheet; 1.016-6.3 mm
- Temper
- T761
- Heat treatment
- solution heat treated and overaged to T76 condition
- Product form
- bare sheet
- Thickness / diameter range
- 0.040-0.248 in (1.016-6.3 mm), within the 0.040-0.249 in table bands
- Test direction
- L and LT
- Processing route
- wrought high-purity heat-treatable aluminum-zinc sheet
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI