| Property |
PH13-8Mo H1000 bar (MIL-HDBK-5H)
PH13-8Mo H1000; bar; thickness/diameter <203.2 mm | bar
|
|---|---|
| Density |
7723 kg/m^3
Density
Historical Nominal
PH13-8Mo H1000; bar; thickness/diameter <203.2 mm; A-basis strengths; S-basis elongation
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
195.122 GPa
Young's modulus
Historical Nominal
PH13-8Mo H1000; bar; thickness/diameter <203.2 mm; A-basis strengths; S-basis elongation
|
| Shear modulus |
75.842 GPa
Shear modulus
Historical Nominal
PH13-8Mo H1000; bar; thickness/diameter <203.2 mm; A-basis strengths; S-basis elongation
|
| Poisson's ratio |
0.28 -
Poisson's ratio
Historical Nominal
PH13-8Mo H1000; bar; thickness/diameter <203.2 mm; A-basis strengths; S-basis elongation
|
| Yield strength |
1310.004 MPa
Tensile yield strength, L
Historical Public Release Table Value
PH13-8Mo H1000; bar; thickness/diameter <203.2 mm; A-basis strengths; S-basis elongation; L direction
1310.004 MPa
Tensile yield strength, LT
Historical Public Release Table Value
PH13-8Mo H1000; bar; thickness/diameter <203.2 mm; A-basis strengths; S-basis elongation; LT direction
1378.951 MPa
Compressive yield strength, L
Historical Public Release Table Value
PH13-8Mo H1000; bar; thickness/diameter <203.2 mm; A-basis strengths; S-basis elongation; L direction
1378.951 MPa
Compressive yield strength, LT
Historical Public Release Table Value
PH13-8Mo H1000; bar; thickness/diameter <203.2 mm; A-basis strengths; S-basis elongation; LT direction
|
| Tensile strength |
1385.846 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
PH13-8Mo H1000; bar; thickness/diameter <203.2 mm; A-basis strengths; S-basis elongation; L direction
1385.846 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
PH13-8Mo H1000; bar; thickness/diameter <203.2 mm; A-basis strengths; S-basis elongation; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|