Metal
PH13-8Mo H1000 bar (MIL-HDBK-5H)
Historical public-release A-basis bar reference for PH13-8Mo H1000.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 7723 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 1385.846 | MPa |
| Tensile yield strength, L | 1310.004 | MPa |
| Ultimate tensile strength, LT | 1385.846 | MPa |
| Tensile yield strength, LT | 1310.004 | MPa |
| Compressive yield strength, L | 1378.951 | MPa |
| Compressive yield strength, LT | 1378.951 | MPa |
| Ultimate shear strength | 806.687 | MPa |
| Elongation, L | 10 | % |
| Elongation, LT | 10 | % |
| Ramberg-Osgood exponent, tension L | 17 | - |
| Ramberg-Osgood exponent, compression L | 17 | - |
| Young's modulus | 195.122 | GPa |
| Compression modulus | 202.706 | GPa |
| Shear modulus | 75.842 | GPa |
| Poisson's ratio | 0.28 | - |
Units
Condition
- Condition
- PH13-8Mo H1000; bar; thickness/diameter <203.2 mm
- Temper
- H1000
- Heat treatment
- solution treated and aged to H1000; verify AMS 5629 schedule
- Product form
- bar
- Thickness / diameter range
- <8 in (203.2 mm); includes the <=50 mm private-catalog scope
- Test direction
- L and transverse values as tabulated
- Processing route
- VIM plus CEVM precipitation-hardening stainless bar
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI